Adhesive TRS 2002 New

Cements

Adhesive TRS 2002 NEW is a two-part cold vulcanizing cement based on CR (polychloroprene rubber). Bonds rubber to rubber, rubber to fabric, rubber to metal, fabric to fabric, metal to fabric. The main difference of TRS 2002 NEW cement from
TRS 2002 cement is the replacement of trichloroethylene with tetrachloroethylene, a safer organic compound for human organism. Like trichloroethylene, tetrachloroethylene neither ignites nor explodes. TRS 2002 NEW adhesive may be used for works in mines or underground premises.

Use: repair and joining of rubber-fabric conveyor belts, rubber coating of metal surfaces, pulley lagging.

Attention: TRS 2002 NEW contents methylenechloride and may cause vapor pressure in heat. Avoid hot storage.Cool down to room temperature before use. Open tins,cans or drums carefully when cement was hot!

Characteristics

• Base: CR - polychloroprene rubber
• Solvent: tetrachloroethylene, dichloromethane
• Specific density: 1.45 g/m3
• Dynamic viscosity: approx. 3200-3800 mPa·s
• Colour: dark grey
• Shelf life: 2 years

Recommendations

• Working temperature: +15/ +30 ºC
• Hardener: TRS 1000 M
• Ratio: 40 g of hardener M per 1 kg of cement
• Pot life: 1-2 hours
• Layer active time: approx. 20 min. at 20 ºC
• Application quantity: 300 g/m² per coat
• Vulcanizing time: approx. 24 hours

Recommended technology of applying the adhesive mixture on the surfaces to be bonded:

• rubber/ rubber-cord materials/ fabric: 2 layers;
• rubber with bonding layer: 1 layer;
• primed metal: 1 layer.

Please see catalog for technical information.